Manufacturer of Ceramic Bodies and Clays for Modelling
  • PRLF firing colour
    PRLF firing colour
    PRLF
    Ref.11 220 001 | EAN8422830112012
    High fire grogged “Lila” 0-0.5 mm

    High fire “Lila” body with 40% fine grog 0-0.5 mm. Formulated for artistic ceramics, it is ideal for sculpture, murals and Raku pieces. Known as “Lila” because of its raw colour (Spanish word that means “lilac”). The high content of grog confers a beautiful textured surface and an excellent behaviour during drying and firing. Its amazing firing colour, with different tones of dark toasted brown, highlights the relief of the piece, and becomes an ideal artistic mean of expression. Available in extruded body (moist form).

    Firing range: 1240-1300ºC
    Biscuit temperature: 1000ºC
    Water content: 19%
    Plasticity (IP Atterberg): 19
    Carbonate content (CaCO3): 0%
    Drying shrinkage: 6.7%
    Firing shrinkage (1300ºC): 5.0%
    Porosity (water absorption at 1300ºC): 8.8%
    Dry bending strength: 3.1 N/mm2
    Fired bending strength (1300ºC): 26.6 N/mm2
    Thermal coefficient (25-500ºC): 52.3x10^-7ºC^-1
    • Wrapped
    • 12.5 kg
  • PRLM firing colour
    PRLM firing colour
    PRLM
    Ref.11 230 001 | EAN8422830112029
    High fire grogged “Lila” 0-1.5 mm

    High fire “Lila” body with 40% coarse grog 0-1.5 mm. Formulated for artistic ceramics, it is ideal for large sculptural works, murals and big Raku pieces. Known as “Lila” because of its raw colour (Spanish word that means “lilac”). The high content of grog confers a beautiful rugged texture and an excellent behaviour during drying and firing. Its amazing firing colour, with different tones of dark toasted brown, highlights the relief of the piece, and becomes an ideal artistic mean of expression. Available in extruded body (moist form).

    Firing range: 1240-1300ºC
    Biscuit temperature: 1000ºC
    Water content: 19%
    Plasticity (IP Atterberg): 19
    Carbonate content (CaCO3): 0%
    Drying shrinkage: 6.0%
    Firing shrinkage (1300ºC): 4.8%
    Porosity (water absorption at 1300ºC): 7.2%
    Dry bending strength: 2.5 N/mm2
    Fired bending strength (1300ºC): 20.2 N/mm2
    Thermal coefficient (25-500ºC): 54.1x10^-7ºC^-1