    High fire grogged black 0-0.2 mm

    High fire black body with 40% impalpable grog 0-0.2 mm. Formulated for artistic ceramics, it is ideal for wheel-throwing and modelling smooth pieces with fine details. The high content of grog confers an excellent behaviour during drying and firing. Its beautiful and intense black firing colour in oxidising atmosphere is very exclusive of PRN range and becomes an ideal artistic mean of expression. In reducing atmosphere, metallic effects with shades of blue are obtained. Suitable for tableware (food-safe), according to ISO 6486. Available in extruded body (moist form).

    Firing range: 1200-1240ºC
    Biscuit temperature: 1000ºC
    Water content: 21%
    Plasticity (IP Atterberg): 22
    Carbonate content (CaCO3): 0%
    Drying shrinkage: 7.0%
    Firing shrinkage (1240ºC): 7.1%
    Porosity (water absorption at 1240ºC): 1.3%
    Dry bending strength: 4.6 N/mm2
    Fired bending strength (1240ºC): 33.3 N/mm2
    Thermal coefficient (25-500ºC): 51.1x10^-7ºC^-1
    • Wrapped
    • 12.5 kg
    Recommendations for use with glazes
    Use zinc-free (Zn-free) glazes to prevent from unexpected reactions such as bubbling or color changes. Other elements that can react are zirconium (Zr) and tin (Sn). We recommend consulting your usual glaze supplier to ensure proper suitability with this ceramic clay body.
  • PRNF
    PRNF
    PRNF
    Ref.13 620 001 | EAN8422830136018
    High fire grogged black 0-0.5 mm

    High fire black body with 40% fine grog 0-0.5 mm. Formulated for artistic ceramics, it is ideal for sculpture. The high content of grog confers a beautiful textured surface and an excellent behaviour during drying and firing. Its beautiful and intense black firing colour in oxidising atmosphere is very exclusive of PRN range and becomes an ideal artistic mean of expression. In reducing atmosphere, metallic effects with shades of blue are obtained. Available in extruded body (moist form).

    Firing range: 1200-1260ºC
    Biscuit temperature: 1000ºC
    Water content: 21%
    Plasticity (IP Atterberg): 22
    Carbonate content (CaCO3): 0%
    Drying shrinkage: 7.0%
    Firing shrinkage (1260ºC): 4.5%
    Porosity (water absorption at 1260ºC): 9.4%
    Dry bending strength: 2.0 N/mm2
    Fired bending strength (1260ºC): 27.5 N/mm2
    Thermal coefficient (25-500ºC): 55.8x10^-7ºC^-1
    • Wrapped
    • 12.5 kg
    Recommendations for use with glazes
    Use zinc-free (Zn-free) glazes to prevent from unexpected reactions such as bubbling or color changes. Other elements that can react are zirconium (Zr) and tin (Sn). We recommend consulting your usual glaze supplier to ensure proper suitability with this ceramic clay body.
  • PRNM
    PRNM
    PRNM
    Ref.13 630 001 | EAN8422830136025
    High fire grogged black 0-1.5 mm

    High fire black body with 40% coarse grog 0-1.5 mm. Formulated for artistic ceramics, it is ideal for large sculpturak works and murals. The high content of grog confers a beautiful rugged texture and an excellent behaviour during drying and firing. Its beautiful and intense black firing colour in oxidising atmosphere is very exclusive of PRN range and becomes an ideal artistic mean of expression. In reducing atmosphere, metallic effects with shades of blue are obtained. Available in extruded body (moist form).

    Firing range: 1200-1260ºC
    Biscuit temperature: 1000ºC
    Water content: 21%
    Plasticity (IP Atterberg): 22
    Carbonate content (CaCO3): 0%
    Drying shrinkage: 7.0%
    Firing shrinkage (1260ºC): 3.6%
    Porosity (water absorption at 1260ºC): 9.8%
    Dry bending strength: 2.0 N/mm2
    Fired bending strength (1260ºC): 22.0 N/mm2
    Thermal coefficient (25-500ºC): 50.3x10^-7ºC^-1
    • Wrapped
    • 12.5 kg
    Recommendations for use with glazes
    Use zinc-free (Zn-free) glazes to prevent from unexpected reactions such as bubbling or color changes. Other elements that can react are zirconium (Zr) and tin (Sn). We recommend consulting your usual glaze supplier to ensure proper suitability with this ceramic clay body.
  • PRNG
    PRNG
    PRNG
    Ref.13 643 001 | EAN8422830136049
    High fire grogged black 1-3 mm

    High fire black body with very coarse grog 1-3 mm. Formulated for artistic ceramics, it is ideal for extra large sculptural work and for pieces with high artistic expression. The big content of grog confers an interesting high rugged texture and an excellent behaviour during drying and firing. Its beautiful and intense black firing colour in oxidising atmosphere is very exclusive of PRN range and becomes an ideal artistic mean of expression. In reducing atmosphere, metallic effects with shades of blue are obtained. Available in extruded body (moist form).

    Firing range: 1200-1260ºC
    Biscuit temperature: 1000ºC
    Water content: 20%
    Plasticity (IP Atterberg): 22
    Carbonate content (CaCO3): 0%
    Drying shrinkage: 6.5%
    Firing shrinkage (1260ºC): 4.4%
    Porosity (water absorption at 1260ºC): 7.8%
    Dry bending strength: 3.0 N/mm2
    Fired bending strength (1260ºC): 17.7 N/mm2
    Thermal coefficient (25-500ºC): 51.3x10^-7ºC^-1
    • Wrapped
    • 12.5 kg
    Recommendations for use with glazes
    Use zinc-free (Zn-free) glazes to prevent from unexpected reactions such as bubbling or color changes. Other elements that can react are zirconium (Zr) and tin (Sn). We recommend consulting your usual glaze supplier to ensure proper suitability with this ceramic clay body.