ZUMAIA refractaria gris 0-0.5mm 12.5kg
ZUMAIA refractaria gris 0-0.5mm 12.5kg
ZUMAIA refractaria gris 0-0.5mm 12.5kg
ZUMAIA refractaria gris 0-0.5mm 12.5kg
ZUMAIA refractaria gris 0-0.5mm 12.5kg
ZUMAIA refractaria gris 0-0.5mm 12.5kg
ZUMAIA refractaria gris 0-0.5mm 12.5kg
ZUMAIA refractaria gris 0-0.5mm 12.5kg
ZUMAIA refractaria gris 0-0.5mm 12.5kg
ZUMAIA refractaria gris 0-0.5mm 12.5kg
ZUMAIA refractaria gris 0-0.5mm 12.5kg
ZUMAIA refractaria gris 0-0.5mm 12.5kg
ZUMAIA refractaria gris 0-0.5mm 12.5kg
ZUMAIA refractaria gris 0-0.5mm 12.5kg

ZUMAIA grey sculpture 0-0.5mm 12.5kg

Grey sculpture 0-0.5 mm

 

Grey sculpture clay with 40% fine grog 0-0.5 mm (up to 35 Mesh). Formulated for artistic and decorative ceramics, it is ideal for sculpture and pieces for outdoors (garden pots, tiles, etc.). The high content of grog confers a beautiful textured surface and an excellent behaviour during drying and firing. Depending on the firing temperature, it develops an interesting range of greys, from cement to dark grey, which satisfies the most avant-garde trends in artistic and decorative ceramics. Available in extruded body (moist form).

Firing range: 1200-1300ºC / Cone 5-10
Biscuit temperature: 1000ºC / Cone 06
Water content: 17%
Plasticity (IP Atterberg): 16
Carbonate content (CaCO3): 0%
Drying shrinkage: 5.3%
Firing shrinkage 1300ºC: 4.3%
Porosity (water absorption) at 1300ºC: 4.5%
Dry bending strength: 2.8 N/mm2
Fired bending strength (1300ºC): 37.8 N/mm2
Thermal coefficient 1250ºC (25-500ºC): 61.6x10^-7ºC^-1

Brand
SIO-2
Firing
Ceramic kiln high fire
Weight/Volume
12,5 kg
Grog
Fine grog
State
Moist form (plastic body)
Stiffness
4 throwing and modelling
145200010000
No reviews